Low temperature chemical synthesis of Ni-Zn ferrite nanoparticles
B. Parvatheeswara Rao
, O. F. Caltun
,
Cheolgi Kim
Department of Physics and Chemistry
Andhra University
Chungnam National University
Research output
:
Contribution to journal
›
Article
›
peer-review
2
Scopus citations
Overview
Fingerprint
Fingerprint
Dive into the research topics of 'Low temperature chemical synthesis of Ni-Zn ferrite nanoparticles'. Together they form a unique fingerprint.
Sort by
Weight
Alphabetically
Chemistry
Reaction Temperature
100%
Nanoparticle
100%
Synthesis (Chemical)
100%
Gel
55%
Sample
44%
Magnetization
33%
Alcohol
33%
Citric Acid
33%
Particle Size
22%
Phase Composition
22%
Metal
22%
Amount
22%
Transmission Electron Microscopy
22%
Water Type
11%
Procedure
11%
Heat
11%
Aqueous Solution
11%
Lattice Parameter
11%
Bearing
11%
Material Science
Temperature
100%
Ferrite
100%
Chemical Synthesis
100%
Poly Vinyl Alcohol
33%
Sol-Gel
33%
Saturation
22%
Metal
22%
Gel
22%
Powder
22%
Solution
11%
X-Ray Diffraction
11%
Magnetometer
11%
Lattice Constant
11%
Fine Particle
11%
Crystallite Size
11%
Bearing
11%
Physics
Temperature
100%
Ferrite
100%
Shapes
22%
Magnetization
22%
Matrix
22%
Metal
22%
Gels
22%
Independent Variables
11%
Ratios
11%
Cores
11%
Water
11%
Value
11%
Estimates
11%
Transmission Electron Microscopy
11%
Saturation Magnetization
11%
Particle Size
11%
Heat
11%
Combustion
11%
Chemical Engineering
Nanoparticle
100%
Temperature
100%
Gel
55%
Polyvinyl Alcohol
33%
Citric Acid
33%
Combustion
11%